| Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Higher viscosity version of FC 2123 Medium viscosity Process targets: transfer and compression molding, bonding and calendering Proprietary incorporated cure technology Excellent release and hot tear properties essential for demolding complex geometric profiles and parts containing severe undercuts&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Good stripping performance,Agglomerability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | Internal Method |
| Mooney viscosity | |||
| ML 1+10，121℃ | 41 | MU | Internal Method |
| Fluorine content | 66 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 70 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 17.0 | MPa | ASTM D412A |
| 100% strain | 4.20 | MPa | ASTM D412A |
| Tensile strain | |||
| fracture | 260 | % | ASTM D412A |
| Compression deformation | ASTM D1414 | ||
| 200℃，70 hr | 18 | % | ASTM D1414 |
| 200℃，70 hr | 17 | % | ASTM D1414 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |