3M™ Dyneon™ Fluoroelastomer FE 5624Q

About
3M™ Dyneon™ Fluoroelastomer FE 5624Q is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5624Q has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Proprietary incorporated cure technology Process targets: injection and transfer moulding, extrusion and calendering Excellent mould release – can be used in automated injection moulding equipment Fast curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q Improved cure technology helps promote more consistent part size from successive moulding cycles Improved scorch resistance at high moulding temperatures Clean running Compounds prepared from Dyneon FE 5624Q can be formulated to meet Mil-R-83248 Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5624Q is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.&&

About

3M™ Dyneon™ Fluoroelastomer FE 5624Q is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5624Q has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Proprietary incorporated cure technology Process targets: injection and transfer moulding, extrusion and calendering Excellent mould release – can be used in automated injection moulding equipment Fast curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q Improved cure technology helps promote more consistent part size from successive moulding cycles Improved scorch resistance at high moulding temperatures Clean running Compounds prepared from Dyneon FE 5624Q can be formulated to meet Mil-R-83248 Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5624Q is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.&&

Product Description
Generic	氟橡胶
Material Status	Commercial: Active
Features	Good stripping performance,Fast Cure
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.80	g/cm³	Internal Method
Mooney viscosity
ML 1+10，121℃	29	MU	Internal Method
Fluorine content	66	%	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	78		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength	15.4	MPa	ASTM D412A
100% strain	6.50	MPa	ASTM D412A
Tensile strain
fracture	210	%	ASTM D412A
Compression deformation			ASTM D1414
200℃，70 hr	20	%	ASTM D1414
200℃，70 hr	15	%	ASTM D1414

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.