| About |
|---|
| Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Medium viscosity Process targets: injection and transfer molding and calendering Improved chemical resistance compared to lower percent fluorine fluoropolymers Excellent compression set resistance compared to lower percent fluorine fluoropolymers Proprietary incorporated cure technology&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Good Compression Set,Copolymer |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.85 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 37 | MU | |
| Fluorine content | 69 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 77 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 15.2 | MPa | |
| 100% strain | 4.83 | MPa | |
| Tensile strain | |||
| fracture | 260 | % | |
| Compression deformation | |||
| 200℃，70 hr | 19 | % | ASTM D395B |
| MH（177℃） | 2.30 | J | |
| ML（177℃） | 0.136 | J | |
| t’50（177℃） | 2.1 | min | |
| t’90（177℃） | 2.9 | min | |
| ts2（177℃） | 1.6 | min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tr10 | -8 | ℃ | ASTM D1329 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |