| 3M™ Dyneon™ Fluoroelastomer FX 9194 is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FX 9194 has an incorporated bisphenol cure system. Special Features Composition: terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene Proprietary incorporated cure technology Low compression set Process targets: compression, injection and transfer moulding High elongation Typical Applications 3M™ Dyneon™ Fluoroelastomer FX 9194 is suitable for the manufacture of moulded goods.&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good Tensile Strength,Terpolymer |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.86 | g/cm³ | Internal Method |
| Mooney viscosity | |||
| ML 1+10，121℃ | 52 | MU | Internal Method |
| Fluorine content | 69 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 77 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 16.5 | MPa | ASTM D412A |
| 100% strain | 4.70 | MPa | ASTM D412A |
| Tensile strain | |||
| fracture | 250 | % | ASTM D412A |
| Compression deformation | ASTM D1414 | ||
| 200℃，70 hr | 30 | % | ASTM D1414 |
| 200℃，70 hr | 27 | % | ASTM D1414 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |