3M™ Dyneon™ Fluoroplastic FEP FLEX6309Z is a fully fluorinated copolymer comprising tetrafluoroethylene and hexafluoropropylene. It was developed mainly for wire and cable extrusion and features greatly enhanced flexibility and stress cracking behavior. Special Features Excellent dielectric properties High thermal stability Service temperature rating up to more than 200 °C Outstanding chemical resistance Wide processing window Greatly enhanced flex life properties Extremely low flammability (high LOI) Smooth surface Excellent anti-stick properties Low coefficient of friction Very high weathering and UV stability Improved mechanical properties&& |
Product Description | |
---|---|
Generic | FEP |
Material Status | Commercial: Active |
Features | Good Rigidity,Weather resistance is good,No viscosity,Good flexibility,Low coefficient of friction,Copolymer,Solvent resistance,Heat Stabilized,High ESCR |
Availabilitys | North America,Europe |
Process Methods | Extrusion |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 2.14 | g/cm³ | ISO 12086 |
Melt Flow Rate | |||
372℃,5.0kg | 9.0 | g/10min | ISO 1133 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
Tensile modulus | 630 | MPa | ISO 527-2 |
tensile strength | |||
Fracture, 23 ℃ | 30.0 | MPa | ISO 527-2 |
Tensile strain | |||
Fracture, 23 ℃ | 350 | % | ISO 527-2 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Melting temperature | 255 | ℃ | ISO 12086 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Dielectric strength | |||
0.25 mm | 65 | kV/mm | ASTM D149 |
Dielectric constant | ASTM D150 | ||
23 ℃,1 MHz | 2.05 | ASTM D150 | |
23 ℃,9.40 GHz | 2.04 | ASTM D150 | |
Dissipation factor | ASTM D150 | ||
1 MHz | 5.0E-4 | ASTM D150 | |
9.4 GHz | 3.0E-4 | ASTM D150 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Extreme oxygen index | > 95 | % | ASTM D2863 |
Supplementary information | Nominal value | Unit | Test method |
---|---|---|---|
MIT flexural strength (double folds, 200.0 µ m) | 110000 | ASTM D2176 |
Process Conditions | |||
---|---|---|---|
Extrusion | Nominal value | Unit | Test method |
Barrel 1 zone temperature | 330 | °C | |
Barrel 2 zone temperature | 345 | °C | |
Barrel 3 zone temperature | 360 | °C | |
Barrel 4 zone temperature | 370 | °C | |
Barrel 5 zone temperature | 385 | °C | |
Nozzle temperature | 395 | °C |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |