| About |
|---|
| 30% GLASS FIBER REINFORCED POLYAMIDE 66 FOR HIGH STIFFNESS AND DIMENSIONAL STABILITY,FLAME RETARDANT.&& |
| Product Description | |
|---|---|
| Generic | PFA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.15 | g/cm³ | ISO 12086 |
| Melt Flow Rate | |||
| 372℃，5.0kg | 2.0 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 308 | ℃ | ISO 12086 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | > 95 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 60 | ASTM D2240 , ISO 868 | |
| tensile strength | |||
| Fracture, 23 ℃ | 34.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 360 | % | ISO 527-2 |
| Bending modulus | 550 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 360 to 390 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |