| PVDF is ideal for multiple applications across a wide array of industries. Widely used in the chemical processing, wire and cable, semiconductor, and oil and gas industries, PVDF is also gaining recognition in automotive, building, electronics, food processing, pharmaceutical and battery applications. PVDF 11008/0003 combines excellent chemical resistance, dimensional stability and excellent flame and smoke resistance with a moderate degree of flexibility. (For applications requiring high degrees of flexibility, see our 30000 series copolymers.) PVDF 11008/0003 has set the standard for plenum rating jacketing and tubes, consistently achieving UL 150°C rating in numerous cable constructions and fiber raceway designs. Features and Benefits PVDF 11008/0003 is a copolymer of VF 2 and HFP (hexafluoropropylene) Improved flexibility over PVDF homopolymers Very low smoke and low flame generation Ideal for applications where high strength and a moderate degree of flexibility are required Ideal for high speed extrusion Excellent weatherability Good chemical resistance Long term use temperatures up to 150°C Processable using most conventional thermoplastic conversion techniques&& |
| Product Description | |
|---|---|
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,Low smoke,Good Dimensional Stability,Low odor,Flame Characteristics,Low liquid permeability,Copolymer,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.78 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | |
| 230℃，5.0kg | 24 | g/10min | |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 52.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 800 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1000 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 160 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | |||
| 23℃ | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 1 MHz | 7.00 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 65 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.079 in/min |
| 4. Voltage <1V, after 2 Minutes - 500V |
| 5. Intensity = 10 mA, after 2 Minutes |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |