| About |
|---|
| 3M™ Dyneon™ PVDF 11010/0000 is a copolymer of VF 2 and HFP (hexafluoropropylene). Recommended for flared tubing, it combines excellent chemical resistance, and dimensional stability with a moderate degree of flexibility. PVDF is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, food processing, and pharmaceutical equipment and battery applications. Features and Benefits Good flexibility and mechanical strength in extruded tubing Flareability of extruded tubing Good chemical resistance to acids, bases, alcohols&& |
| Product Description | |
|---|---|
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,Alkali resistant,Low smoke,Good Dimensional Stability,Ethanol tolerance,Low odor,Flame Characteristics,Acidproof,Low liquid permeability,Copolymer,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.78 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | |
| 230℃，5.0kg | 6.0 | g/10min | |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 27.0 | MPa | |
| Fracture, 23 ℃ | 30.0 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 400 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 900 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 37.0 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed, 4.0 mm | 100 | ℃ | |
| 1.8 MPa, annealed, 4.0 mm | 52.0 | ℃ | |
| Vicat Softening Temp | 150 | ℃ | ISO 306/A |
| Melting peak temperature | 160 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |