| About |
|---|
| Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, pharmaceutical and batteries. 3M™ Dyneon™ PVDF 6008/0001 is easily processed under a variety of conventional thermoplastic conversion techniques, being particularly suitable for extrusion. PVDF 6008/0001 is inherently pure and chemically resistant against a variety of aggressive fluids and solvents. PVDF 6008/0001 exhibits excellent dimensional stability, abrasion resistance and high strength, and maintains its mechanical properties at elevated temperature. Features and Benefits Excellent chemical resistance to a variety of aggressive fluids and solvents Smooth, anti-fouling surfaces Good permeation resistance Injection molding grade Excellent strength and dimensional stability Good color stability&& |
| Product Description | |
|---|---|
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High purity,Good Dimensional Stability,Good color stability,Good wear resistance,Solvent resistance,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.78 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ASTM D1238 | ||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| 230℃，5.0kg | 24 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 3.0 | % | |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃ | 55.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 42.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 23 ℃ | 7.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 35 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2200 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D3418 | ||
| 0.45 MPa, annealed, 4.0 mm | 147 | ℃ | ASTM D3418 |
| 1.8 MPa, unannealed, 4.0 mm | 112 | ℃ | ASTM D3418 |
| Melting peak temperature | 174 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |