3M™ Dyneon™ Perfluoroelastomer PFE 4131TZ

About
3M™ Dyneon™ PFE 4131TZ is an incorporated cure high temperature perfluorelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per ASTM D1418. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Features and Benefits PFE 131TZ compounded with curative for ease in manufacturing Upper use temperature of 315°C Excellent compression set resistance Can be compounded to pass AMS 7257D Ideal for dry side (thermal processes) semiconductor applications, including plasma, and high temperature CPI and aerospace applications Low metal ion content with low extractables&&

About

3M™ Dyneon™ PFE 4131TZ is an incorporated cure high temperature perfluorelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per ASTM D1418. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Features and Benefits PFE 131TZ compounded with curative for ease in manufacturing Upper use temperature of 315°C Excellent compression set resistance Can be compounded to pass AMS 7257D Ideal for dry side (thermal processes) semiconductor applications, including plasma, and high temperature CPI and aerospace applications Low metal ion content with low extractables&&

Product Description
Generic	PFE
Material Status	Commercial: Active
Features	Low extract,Low (to None) Ion Content,Good Compression Set,High Heat Resistance,Solvent resistance,Heat Stabilized
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.00	g/cm³
Mooney viscosity
ML 1+10，121℃	100	MU

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	81		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength	17.1	MPa	ASTM D412
100% strain	12.1	MPa	ASTM D412
Tensile strain
fracture	160	%	ASTM D412
Compression deformation
232℃，70 hr	17	%
232℃，168 hr	33	%
300℃，70 hr	39	%
300℃，168 hr	46	%
MH	1.99	J
ML	0.107	J
t’50	2.9	min
t’90	6.0	min
ts2	1.7	min

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	-35.0	℃

Supplementary information	Nominal value	Unit	Test method
Tr10	-2	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.