3M™ Dyneon™ Perfluoroelastomer PFE 60Z

About
3M™ Dyneon™ PFE 60Z is a technically advanced peroxide curable perfluoroelastomer, designed to meet the challenges of demanding sealing applications. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Low viscosity provides good mold flow and is ideal for molding large parts. It is classified as FFKM per ASTM D1418. Features and Benefits Improved mold flow and knitting over 3M™ Dyneon™ PFE 80Z and PFE 90Z Ideal for wet chemical, fluid handling, cleaning and chemical etching processes, and for large parts for CPI and aerospace Good compression set resistance Upper use temperature of 220°C Low metal ion content with low extractables in a wide range of chemicals Can be utilized to adjust Mooney when using PFE 80Z or PFE 90Z&&

About

3M™ Dyneon™ PFE 60Z is a technically advanced peroxide curable perfluoroelastomer, designed to meet the challenges of demanding sealing applications. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Low viscosity provides good mold flow and is ideal for molding large parts. It is classified as FFKM per ASTM D1418. Features and Benefits Improved mold flow and knitting over 3M™ Dyneon™ PFE 80Z and PFE 90Z Ideal for wet chemical, fluid handling, cleaning and chemical etching processes, and for large parts for CPI and aerospace Good compression set resistance Upper use temperature of 220°C Low metal ion content with low extractables in a wide range of chemicals Can be utilized to adjust Mooney when using PFE 80Z or PFE 90Z&&

Product Description
Generic	PFE
Material Status	Commercial: Active
Features	Low extract,Low (to None) Ion Content,Good liquidity,Low Viscosity,Good Compression Set,Solvent resistance,Heat Stabilized
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.00	g/cm³
Mooney viscosity
ML 1+10，121℃	60	MU

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	75		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength	17.9	MPa	ASTM D412
100% strain	11.0	MPa	ASTM D412
Tensile strain
fracture	170	%	ASTM D412
Compression deformation
200℃，70 hr	49	%
200℃，168 hr	55	%
230℃，70 hr	56	%
230℃，168 hr	68	%
MH	1.51	J
ML	0.226	J
t’50	48.0	sec
t’90	1.5	min
ts2	36.0	sec

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	-35.0	℃

Supplementary information	Nominal value	Unit	Test method
Tr10	-2	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.