3M™ Dyneon™ PTFE TF 2073Z

About
3M™ Dyneon™ PTFE Fine Powder TF 2073Z is recommended for the manufacture of micro tubing, wire and cable insulations. Special Features Meets ASTM D 4895 Type I, Grade 1, Class C classification High molecular weight PTFE powder produced by emulsion polymerisation Reduces lubricant consumption (1 part by weight per 100 parts by weight PTFE, compared with TF 2072Z) Wide processing window due to large reduction ratio (RR) range Reduced extruder load because of lower extrusion pressure Far more cost-effective processing because of the possible use of larger pre-forms Processing by standard paste extrusion methods Excellent chemical inertness Low friction behaviour High flame retardance Exceptional temperature resistance Very good electrical properties&&

About

3M™ Dyneon™ PTFE Fine Powder TF 2073Z is recommended for the manufacture of micro tubing, wire and cable insulations. Special Features Meets ASTM D 4895 Type I, Grade 1, Class C classification High molecular weight PTFE powder produced by emulsion polymerisation Reduces lubricant consumption (1 part by weight per 100 parts by weight PTFE, compared with TF 2072Z) Wide processing window due to large reduction ratio (RR) range Reduced extruder load because of lower extrusion pressure Far more cost-effective processing because of the possible use of larger pre-forms Processing by standard paste extrusion methods Excellent chemical inertness Low friction behaviour High flame retardance Exceptional temperature resistance Very good electrical properties&&

Product Description
Generic	PTFE
Material Status	Commercial: Active
Features	Good Electrical Properties,Low coefficient of friction,Flame Characteristics,High molecular weight
Availabilitys	North America,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.17	g/cm³	ISO 12086
Apparent density	0.49	g/cm³	ISO 60
Average particle size	400	µm	ISO 13320

film	Nominal value	Unit	Test method
tensile strength	35.0	MPa	ISO 527-3
Tensile strain
fracture	460	%	ISO 527-3

Supplementary information	Nominal value	Unit	Test method
Extrusion pressure
Reduction Ratio 1600	26.0	MPa	ASTM D4895
Reduction Ratio	50.0:1.0 to 4400.0:1.0		Internal Method

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.