| About |
|---|
| Features and Benefits Meets ASTM D4894 Type lll, Grade 2 resin Molding and ram extrusion powder with very good free-flow properties Good metering properties Good mold filling behavior Improved particle coalescence Denser polymer structure Lower permeability Substantially lower deformation under load Improved weldability Good electrical and mechanical properties Increased modulus of elasticity&& |
| Product Description | |
|---|---|
| Generic | PTFE |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Welding |
| Availabilitys | North America,Europe |
| Process Methods | Plunger extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.16 | g/cm³ | ASTM D4894 |
| Apparent density | 0.83 | g/cm³ | ASTM D4894 |
| Shrinkage rate | |||
| MD | 3.5 | % | ASTM D4894 |
| Average particle size | 450 | µm | ASTM D4894 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 650 | MPa | ASTM D638 |
| tensile strength | 31.7 | MPa | ASTM D4894 |
| Tensile strain | |||
| fracture | 450 | % | ASTM D4894 |
| Load deformation | |||
| 15 MPa | 8.00 | % | |
| 15 MPa | 9.00 | % | |
| 15 MPa | 4.00 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| — | 317 to 337 | ℃ | |
| — | 332 to 352 | ℃ | |
| Operating temperature | -200 to 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 100 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Permanent |
| 3. 100 hrs |
| 4. 24 hrs |
| 5. Second |
| 6. Initial |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |