| 4LAC 10H20800 I is a Standard Flow Recycled Impact Modified ABS&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Renewable resources,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.30 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2600 | MPa | ISO 527-2/5 |
| tensile strength | |||
| Fracture, 23 ℃ | 43.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2/5 |
| Bending modulus | 2600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 70.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 19 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 97.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 97.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 108 | ℃ | ISO 306/B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |