| About |
|---|
| (PC+PET)-blend, 15% mineral filled, easy flow, low coefficient of linear thermal expansion, easy release, injection molding. Molded parts from UT235M having exceptional dimensional stability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Low CLTE,Good Dimensional Stability,Good liquidity,Good stripping performance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 270℃，5 kg | 39.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 2577 | ||
| TD：270℃，3.0 mm | 0.50 to 0.60 | % | ISO 2577 |
| MD：270℃，3.0 mm | 0.50 to 0.60 | % | ISO 2577 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 4500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 67.0 | MPa | ISO 527-2/5 |
| Yield, 23 ℃ | 68.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2/5 |
| Yield, 23 ℃ | 3.5 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 4650 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| 23℃ | 115 | MPa | ISO 178 |
| 3.50% strain, 23 ℃ | 110 | MPa | ISO 178 |
| Bending strain | 5.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 85 | kJ/m² | ISO 179/1eU |
| 23℃ | 85 | kJ/m² | ISO 179/1eU |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -30℃ | 85 | kJ/m² | ISO 180 |
| 23℃ | 85 | kJ/m² | ISO 180 |
| Multi axial instrumented impact energy | |||
| 23℃ | 36.0 | J | ISO 6603-2 |
| Multi axial instrumented peak impact force | |||
| 23℃ | 4500 | N | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 114 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 128 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B120 | 139 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~85℃ | 4.8E-5 | 1/℃ | ISO 11359-2 |
| MD：23~85℃ | 4.5E-5 | 1/℃ | ISO 11359-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm,, MT 70°C, 600 bar |
| 3. 0.079 in/min |
| 4. 2 mm/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |