| About |
|---|
| Continuously manufactured ACRYLITE® Resist sheet is a versatile, thermoplastic material developed for the retail display and glazing markets as well as ther markets requiring strength, appearance and weatherability. High optical quality ACRYLITE® Resist sheet provides the beautiful look of acrylic with much greater impact strength for durability during manufacturing, shipping, and in-store use. Rigid, tough, and lightweight, ACRYLITE® Resist is easily fabricated and machined, including cutting, routing, forming, and cementing. ACRYLITE® Resist is ideal for use in: P-O-P Displays Store Fixtures Glazing General Fabrication&& |
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | SMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,High impact resistance,Machinable,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 40 | J/m | ASTM D256 |
| Drop hammer impact | 4.52 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 71.0 | ℃ | ASTM D648 |
| Continuous use temperature | 71.1 | ℃ | |
| Vicat Softening Temp | 98.9 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 7.9E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | ASTM D635 | ||
| 1.52 mm | 36 | mm/min | ASTM D635 |
| 5.99 mm | 25 | mm/min | ASTM D635 |
| Autoignition temperature | 399 | ℃ | ASTM D1929 |
| Smoke density | ASTM D2843 | ||
| 1.50 mm | 2.2 | % | ASTM D2843 |
| 6.00 mm | 3.8 | % | ASTM D2843 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20° | 140 | ASTM D523 | |
| Refractive index | 1.490 | ASTM D542 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Forming temperature | 132 to 177 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 70 | ASTM D785 | |
| Tensile modulus | 2210 | MPa | ASTM D638 |
| tensile strength | 46.2 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 6.6 | % | ASTM D638 |
| Bending modulus | 2070 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |