| About |
|---|
| DOWLEX™ GM 8480G Polyethylene Resin is suitable for cast stretch film applications with superior extensibility while maintaining good puncture and load retention. Main Characteristics: Superior extensibility Good puncture and load retention&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Membrane puncture resistance | 22.9 | J/cm³ | Internal Method |
| tensile strength | ASTM D882 | ||
| MD, yield | 9.97 | MPa | ASTM D882 |
| TD, yield | 8.49 | MPa | ASTM D882 |
| MD, fracture | 32.3 | MPa | ASTM D882 |
| TD, fracture | 18.9 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 320 | % | ASTM D882 |
| TD, fracture | 360 | % | ASTM D882 |
| Drop hammer impact | 340 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 210 | g | ASTM D1922 |
| TD | 360 | g | ASTM D1922 |
| Film Stretch Performace（On Pallet Puncture） | 53 | N | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Maximum elongation | 340 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 121 | ℃ | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cast |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |