| About |
|---|
| Zytel® 70G30HSL NC010 is a 30% glass reinforced, heat stabilized nylon 66 resin for injection molding. |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.1 | % | ISO 294-4，ISO 2577 |
| TD: Drying | 0.3 | % | ISO 294-4，ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| dry | 10000 | MPa | ISO 527 |
| cond | 7000 | MPa | ISO 527 |
| tensile strength | |||
| fracture | 200 | MPa | ISO 527 |
| Fracture, cond | 130 | MPa | ISO 527 |
| Tensile strain | |||
| fracture | 3.4 | % | ISO 527 |
| Fracture, cond | 5 | % | ISO 527 |
| Tensile creep modulus | |||
| 1h，cond | 6800 | MPa | ISO 899-1 |
| 1000h，cond | 5100 | MPa | ISO 899-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 82 | kJ/m² | ISO 179/1eU |
| 23 ℃, dry | 93 | kJ/m² | ISO 179/1eU |
| -30℃ | 70 | kJ/m² | ISO 179/1eU |
| -30 ℃, dry | 73 | kJ/m² | ISO 179/1eU |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| 23 ℃, dry | 16 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| -30 ℃, dry | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 263 | ℃ | ISO 11357-1/-3 |
| Glass transition temperature, 10 ℃/min, dry | 80 | ℃ | ISO 11357-1/-2 |
| Hot deformation temperature | |||
| 1.8 Mpa | 248 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 261 | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| TD | 22E-6 | K | ISO 11359-1/-2 |
| MD | 107E-6 | K | ISO 11359-1/-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| FMVSS，1mm | 13 | mm/min | ISO 3795 (FMVSS 302) |
| Extreme oxygen index | 24 | % | ISO 4589-1/-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100 Hz | 4.4 | IEC 62631-2-1 | |
| 100 Hz, crystalline | 10.8 | IEC 62631-2-1 | |
| 1 MHz | 4.1 | IEC 62631-2-1 | |
| 1 MHz, crystalline | 4.6 | IEC 62631-2-1 | |
| Dissipation factor | |||
| 100Hz | 70 | E-4 | IEC 62631-2-1 |
| 100Hz，cond | 4600 | E-4 | IEC 62631-2-1 |
| 1MHz | 150 | IEC 62631-2-1 | |
| 1MHz，cond | 650 | IEC 62631-2-1 | |
| Volume resistivity | |||
| desiccation | >1E15 | ohms·cm | IEC 62631-3-1 |
| crystallization | >1E11 | ohms·cm | IEC 62631-3-1 |
| Surface resistivity | |||
| cond | 1E13 | ohms | IEC 62631-3-2 |
| Dielectric strength | |||
| Dry | 38 | kV/mm | IEC 60243-1 |
| crystallization | 32 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 400 | IEC 60112 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 6 | % | ISO 62 |
| Moisture absorption rate | 1.9 | % | Sim. to ISO 62 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |