| About |
|---|
| AvaSpire® AV-651 GF50 is a 50% chopped glass fiber-reinforced polyaryletherketone (PAEK) resin. It has been specifically formulated to provide exceptionally high strength and stiffness at elevated temperatures along with very strong chemical resistance to a broad range of harsh chemical environments encountered across a wide variety of industries and engineering applications. Typical potential applications for AV-651 GF50 include orthopedic and dental instruments, under-the-hood automotive parts, and parts in the chemical and oil and gas industries. This grade is easily injection moldable into precision molded parts. Typical property data provided are based on a limited production history. Beige: AvaSpire® AV-651 GF50 BG 20 Black: AvaSpire® AV-651 GF50 BK 95&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good disinfection,Steam sterilized,Gamma radiation,E-beam disinfection,Biocompatible,Flame Characteristics,High pressure disinfection,High Heat Resistance,Radioactive,Fatigue resistance,Radiation disinfection,Solvent resistance,Resistance to the steam,Ethylene oxide disinfection,Heat sterilization |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 17900 | MPa | ASTM D638 |
| tensile strength | 199 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.1 | % | ASTM D638 |
| Bending modulus | 16500 | MPa | ASTM D790 |
| bending strength | 297 | MPa | ASTM D790 |
| Elongation at break and bending | 2.2 | % | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 960 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.2 mm | 287 | ℃ | ASTM D648 |
| Glass transition temperature | 158 | ℃ | ASTM D3418 |
| Melting peak temperature | 340 | ℃ | ASTM D3417 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 630 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 365 | °C | |
| Barrel middle temperature | 371 | °C | |
| Barrel front temperature | 377 | °C | |
| Nozzle temperature | 382 | °C | |
| Processing (melt) temperature | 366 to 388 | °C | |
| Mold temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |