| About |
|---|
| TRANSMARE® BIO M106 is a non-transparent granulate based on modified polylactic acid Good oxidation-, colour- and molecular weight stability in the melt Biodegradable,/Compostable: TRANSMARE® BIO M106 is based on materials that are certified according to DIN EN 13432:2000-12 and ASTM D 6400:1999 Predominantly based on renewable raw materials TRANSMARE® BIO M106 can be provided in custom colours&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Good color stability,Compostable |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ISO 868 | |
| Tensile modulus | |||
| 4 mm, injection molded | 2600 | MPa | ISO 527-2/50 |
| tensile strength | |||
| Fracture, 4 mm, injection molded | 16.0 | MPa | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 49.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 15 | % | ISO 527-2/50 |
| Yield, 4 mm, injection molding | 2.7 | % | ISO 527-2/50 |
| Bending modulus | |||
| injection molding | 2300 | MPa | ISO 178 |
| bending strength | |||
| injection molding | 37.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40 ℃, injection molding | 2.5 | kJ/m² | ISO 179/1A |
| -20 ℃, injection molding | 3.3 | kJ/m² | ISO 179/1A |
| 0 ℃, injection molding | 4.5 | kJ/m² | ISO 179/1A |
| 23 ℃, injection molding | 5.0 | kJ/m² | ISO 179/1A |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40 ℃, injection molding | 3.0 | kJ/m² | ISO 180-1A |
| -20 ℃, injection molding | 4.0 | kJ/m² | ISO 180-1A |
| 0 ℃, injection molding | 5.5 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 6.4 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 50.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 57.0 | ℃ | ISO 306/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 50 | °C | |
| Drying time – hot air dryer | 4.0 | hr | |
| Dew Point – Hot Air Dryer | -40 | °C | |
| Recommended maximum moisture content | 0.30 | % | |
| Processing (melt) temperature | 150 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |