UNITHENE® LH606

About
UNITHENE LH606 is a high density polyethylene (HDPE) suitably used for injection molding and filament applications. Typical applications are the injection molding of fruit crates, food containers, industrial items such as pallets, transportation crates, housewares, toys and the fine filament extrusion of mosquito nets. UNITHENE LH606 possesses high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH606 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH606 can be easily accomplished after a simple flame, chemical or electronic surface treatment.&&

About

UNITHENE LH606 is a high density polyethylene (HDPE) suitably used for injection molding and filament applications. Typical applications are the injection molding of fruit crates, food containers, industrial items such as pallets, transportation crates, housewares, toys and the fine filament extrusion of mosquito nets. UNITHENE LH606 possesses high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH606 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH606 can be easily accomplished after a simple flame, chemical or electronic surface treatment.&&

Product Description
Supplier	USI
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Good liquidity,Sprayable,Good Tensile Strength
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.962	g/cm³	ASTM D792
Melt Flow Rate	6.0	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	69	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -76.0	℃	ASTM D746
Vicat Softening Temp	127	℃	ASTM D1525
Melting peak temperature	135	℃	ASTM D3418

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	69		ASTM D2240
Tensile modulus
1% cut, molded	971	MPa	ASTM D638
tensile strength			ASTM D638
yield	30.4	MPa	ASTM D638
fracture	21.6	MPa	ASTM D638
Tensile strain
fracture	600	%	ASTM D638
Bending modulus
23℃	971	MPa	ASTM D747

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.