| 40% Glass Reinforced, Impact Modified&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.50 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 12000 | MPa | |
| 120℃ | 6100 | MPa | |
| 160℃ | 3900 | MPa | |
| 200℃ | 3000 | MPa | |
| tensile strength | |||
| fracture | 160 | MPa | |
| Fracture, 120 ℃ | 65.0 | MPa | |
| Fracture, 160 ℃ | 50.0 | MPa | |
| Fracture, 200 ℃ | 40.0 | MPa | |
| Tensile strain | |||
| fracture | 2.4 | % | |
| Fracture, 120 ℃ | 3.9 | % | |
| Fracture, 160 ℃ | 4.4 | % | |
| Fracture, 200 ℃ | 4.5 | % | |
| Bending modulus | |||
| — | 10000 | MPa | |
| 120℃ | 8500 | MPa | |
| 160℃ | 4600 | MPa | |
| 200℃ | 3100 | MPa | |
| bending strength | 230 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 16 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 65 | kJ/m² | |
| 23℃ | 55 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-5 | 1/℃ | |
| MD | 1.5E-5 | 1/℃ | |
| TD | 5.5E-5 | 1/℃ | |
| TD | 1.1E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 33 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 5.00 GHz | 3.80 | IEC 60250 | |
| Dissipation factor | |||
| 5 GHz | 5.5E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |