| About |
|---|
| ABSH2938-P is a medium heat resistance ABS resion for plating , offering high rigidity and high impact.&& |
| Product Description | |
|---|---|
| Supplier | KumhoSunny |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Heat Resistance, Good |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 9.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 23℃ | 0.40 to 0.70 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 37.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 63 | % | ISO 527-2/50 |
| Bending modulus | |||
| 64 mm | 2130 | MPa | ISO 178 |
| bending strength | |||
| 64 mm | 60.0 | MPa | ISO 178 |
| Poisson’s ratio | 0.39 | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 26 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 无断裂 | ISO 179 | |
| 23℃ | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 11 | kJ/m² | ISO 180 |
| 23℃ | 24 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -30℃ | 无断裂 | ISO 180 | |
| 23℃ | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 99.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 86.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 106 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：-40~40℃ | 7.7E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.6E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 235 to 255 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Back pressure | 1.00 to 5.00 | MPa | |
| Screw speed | 30 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Condition: 4 J |
| 4. Condition: 5.5 J |
| 5. 120°C/h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |