| Moplen EP 400H is an heterophasic copolymer especially developed for extrusion applications. Moplen EP 400H exhibits high stiffness, very high impact properties at room and sub-zero temperatures, good dimensional stability and excellent creep and deforming resistance. The main applications of Moplen EP 400H are thermoforming, corrugated board and extrusion blow moulding.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Good Dimensional Stability,Copolymer,low-temperature impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.7 | g/10min | ASTM D1238，ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 1.80 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20℃ | 7.0 | kJ/m² | ISO 179/1e |
| 0℃ | 10 | kJ/m² | ISO 179/1e |
| 23℃ | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 190 | kJ/m² | ISO 179/1eU |
| 0℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 78 | J/m | ASTM D256 |
| 23℃ | 740 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 78.0 | ℃ | ISO 75-2/B |
| Toughness/brittle transition temperature | -55.0 | ℃ | ISO 6603-2 |
| Vicat Softening Temp | |||
| A50 | 153 | ℃ | ISO 306/A50 |
| B50 | 70.0 | ℃ | ISO 306 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 65 | DIN 67530 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 48.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1400 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 29.4 | MPa | ASTM D638 |
| yield | 27.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 9.0 | % | ASTM D638 |
| yield | 8.0 | % | ISO 527-2 |
| fracture | > 50 | % | ISO 527-2 |
| Bending modulus | 1320 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |