| About |
|---|
| ENGAGE™ 8440G Polyolefin Elastomer is an ethylene-octene copolymer that performs well in a wide range of thermoplastic elastomer applications. It is an excellent thermoplastic elastomer for blending and compounding. Main Characteristics: Pellet form Applications: Thermoplastic elastomers Compounding&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.897 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.6 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 93 | ℃ | DOW |
| Glass transition temperature | -33 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 75 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore A1 seconds | 86 | ASTM D2240 | |
| Shore A1 seconds | 36 | ASTM D2240 | |
| tensile strength | |||
| 23℃ | 20.40 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 690 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 6.30 | MPa | ASTM D638 |
| tear strength | |||
| MD | 78.90 | KN/m | |
| Bending modulus | |||
| 23℃ | 54.30 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 3. Die C |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |