| Amodel® AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry. Amodel® AFA-6145 V0 Z offers high flow and short molding cycles, thereby enhancing molding productivity and lowering costs. Black: AFA-6145 V0 Z BK 324 Natural: AFA-6145 V0 Z NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High liquidity,Good Electrical Properties,Flame Characteristics,Solvent resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 0.40 | % | ASTM D955 |
| MD | 0.20 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 193 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.5 | % | ASTM D638 |
| Bending modulus | 15500 | MPa | ASTM D790 |
| bending strength | 276 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 277 | ℃ | ASTM D648 |
| Melting peak temperature | 310 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.59 mm | 23 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 4.10 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.011 | ASTM D150 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.75 mm | PLC 1 | UL 746 | |
| 1.5 mm | PLC 1 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.79 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.045 | % | |
| Barrel rear temperature | 316 to 324 | °C | |
| Barrel front temperature | 327 to 332 | °C | |
| Processing (melt) temperature | 321 to 338 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. This flammability rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |