| Blow Molding Grade, Heat Stabilized&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，10 kg | 2.00 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.50 | % | ISO 62 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 120 | kN/m | ISO 34-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 9.1 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 13 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 63.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 52.0 | ℃ | ISO 306 |
| Melting temperature | 202 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 94 | ||
| Shore A, 15 seconds | 94 | ||
| Shore D, 3 seconds | 50 | ||
| Tensile modulus | 155 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 33.0 | MPa | |
| fracture | 26.8 | MPa | |
| 5% strain | 7.70 | MPa | |
| 5% strain | 8.10 | MPa | |
| 10% strain | 11.7 | MPa | |
| 10% strain | 9.00 | MPa | |
| 10% strain | 12.1 | MPa | |
| 10% strain, 100 ℃ | 4.60 | MPa | |
| 50% strain | 3.90 | MPa | |
| 50% strain | 19.2 | MPa | |
| 100% strain | 14.2 | MPa | |
| 100% strain | 23.2 | MPa | |
| Tensile strain | |||
| fracture | 700 | % | ISO 527-2 |
| Nominal tensile fracture strain | 170 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die Cutting – Normal |
| 3. Die Cutting – Parallel |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |