| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good heat aging resistance,Good Dimensional Stability,Low Viscosity,High Heat Resistance,Good bond,Solvent resistance,Welding,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD | 0.10 | % | Internal Method |
| TD | 1.32 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 54 | J/m | ISO 179 |
| Izod notched impact strength | 520 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 425 | J/m | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 313 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 304 | ℃ | ISO 75 |
| Linear coefficient of thermal expansion | Internal Method | ||
| MD：50~250℃ | 1.4E-5 | 1/℃ | Internal Method |
| TD：50~250℃ | 6.2E-5 | 1/℃ | Internal Method |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10E+15 | ohms·cm | ASTM D257 |
| Surface resistivity | 10E+16 | ohms | |
| Dielectric constant | ASTM D150 | ||
| 1 MHz | 3.9 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 MHz | 0.034 | ASTM D150 | |
| Arc resistance | 130 | sec | ASTM D495 |
| Compared to the leakage tracing index | 145 | V | IEC method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.30 mm, natural color, black | V-0 | UL 94 | |
| Extreme oxygen index | 48 | % | JIS K7201 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Soldering Resistance | 330 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 91 | ASTM D785 | |
| tensile strength | |||
| 150 | MPa | ASTM D638 | |
| 103 | MPa | ISO 527 | |
| Tensile modulus | 11900 | MPa | ISO 527 |
| Tensile strain | |||
| 5.0 | % | ASTM D638 | |
| 3.1 | % | ISO 527 | |
| Bending modulus | ASTM D790 | ||
| 23℃ | 12300 | MPa | ASTM D790 |
| 200℃ | 12900 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| 139 | MPa | ASTM D790 | |
| 153 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Injection speed | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 330 to 350 | °C | |
| Temperature in the middle of the barrel | 350 to 370 | °C | |
| Front temperature of material barrel | 370 to 390 | °C | |
| Nozzle temperature | 370 to 390 | °C | |
| Processing (melt) temperature | 380 | °C | |
| Mold temperature | 40 to 160 | °C | |
| Injection pressure | 120 to 160 | MPa | |
| Maintaining pressure | 40 to 60 | MPa | |
| Back pressure | 1 to 5 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |