| FEATURES Good balance of flow and strength High stiffness USP Class VI certified UL Classification 94 HB (www.UL.com file E57787) APPLICATIONS Medical labware Appliance accessory parts Profile extrusion Cosmetic cases&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,HB |
| Availabilitys | North America,Latin America |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Apparent density | |||
| — | 0.59 to 0.64 | g/cm³ | |
| — | 0.62 to 0.67 | g/cm³ | |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 21 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 93.3 | ℃ | |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.18 mm | 20 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1.00 mm，1 MHz | 2.50 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.590 | ASTM D542 | |
| Transmittance | |||
| 550 nm | 88.0 to 90.0 | % | ASTM D1003 |
| Optical Density – 400-700 nm avg. | 0.0460 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3170 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 49.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 3310 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 76 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 182 to 277 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. without external lubricant |
| 3. with external lubricant |
| 4. 4h/80°C |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 6. Sodium D line |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |