| CYCOLOY C3650 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY C3650 resin is a general purpose resin that is an excellent candidate for a wide variety of applications including cable channels and is verified non-halogen by the DIN VDE 0472/815 standard.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,Flame Characteristics,V-0,5VB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 8.5 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.60 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| 23℃ | 48 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 690 | J/m | ASTM D256 |
| -30℃ | 13 | kJ/m² | ISO 180-1A |
| 0℃ | 15 | kJ/m² | ISO 180-1A |
| 23℃ | 45 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 65.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 88.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 91.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 3.2 mm | 100 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 102 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 108 | ℃ | ISO 306 |
| B120 | 110 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~60℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：23~60℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 35 | kV/mm | IEC 60243-1 |
| 1.6 mm in oil | 25 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | IEC 60250 | |
| 60 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 6.0E-3 | ASTM D150 | |
| 60 Hz | 6.0E-3 | ASTM D150 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 6.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| Extreme oxygen index | 37 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2860 | MPa | ASTM D638 |
| Tensile modulus | 2600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 51.0 | MPa | ASTM D638 |
| yield | 64.8 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/5 |
| yield | 65.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 35 | % | ASTM D638 |
| yield | 4.9 | % | ASTM D638 |
| fracture | 55 | % | ISO 527-2/5 |
| fracture | > 50 | % | ISO 527-2/50 |
| Bending modulus | 2700 | MPa | ISO 178 |
| 50 mm span | 2690 | MPa | ASTM D790 |
| bending strength | 100 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 101 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 124 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 113 | MPa | ISO 2039-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |