Ultramid A3WG7 BK00564 is a 35% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery for industrial items. Applications Typical applications include gear wheels, solenoid valve housings, cable attachments, automotive fuel distributors and components for automotive gear shift.&& |
Product Description | |
---|---|
Supplier | BASF |
Generic | PA66 |
Material Status | Commercial: Active |
Features | High Heat Resistance,Grease resistance |
Availabilitys | North America |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.41 | g/cm³ | ISO 1183 |
Water absorption rate | |||
23℃,24hr | 5.0 | % | ISO 62 |
23℃,50% RH | 1.6 | % | ISO 62 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
23℃ | 200 | MPa | ISO 527-2 |
Tensile strain | |||
Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
Tensile modulus | |||
23℃ | 11500 | MPa | ISO 527-2 |
Bending modulus | |||
23℃ | 10000 | MPa | ISO 178 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, annealed | 250 | ℃ | ISO 75-2/Af |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Volumetric resistance | 1.0E+14 | Ω.cm | IEC 60093 |
Insulation strength | |||
28 | KV/mm | IEC 60243-1 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | |||
0.71mm | HB | UL-94 | |
1.50mm | HB | UL-94 | |
3.00mm | HB | UL-94 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Charpy Notched Impact Strength | |||
23℃ | 11 | kJ/m² | ISO 179/1eA |
Impact strength of cantilever beam notch | |||
23℃ | 12 | kJ/m² | ISO 180-1A |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 80 | °C | |
Drying time | 3-6 | Hr | |
Water content | 0.12 | % | |
Injection temperature | |||
Rear barrel temperature | 270-290 | °C | |
Central temperature of the barrel | 270-290 | °C | |
Barrel front temperature | 270-290 | °C | |
Die temperature | 280-300 | °C | |
Mold temperature | 80-90 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |