| Characteristics: High ethylene control reologhy Random copolymer polypropylene; high cleanness and lot to lot uniformity; very good optical properties and gauge control; with slip and antiblock additives. Recommended for: Cast and TWQ Films heat seal co-extruded layer; conventional film properties modifier; injection molding general purpose applications.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High purity,Smoothness,Optical performance,Controllable rheological,High anti-blocking,Good Gauge Control,Food contact compliance,Random copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 20.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 3.20 mm, injection molding | 14 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, 3.20 mm, injection molded | 621 | MPa | ASTM D790-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 75 | J/m | ASTM D256-A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure B |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |