| About |
|---|
| Infino WP-1069 is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive.&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Africa & Middle East ,Europe,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| – | 1.13 | g/cm³ | ISO 1183 |
| 1.13 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 250℃，10.0kg | 47 | g/10min | ISO 1133 |
| 250℃，10.0kg | 47 | g/10min | ASTM D1238 |
| Shrinkage rate | ISO 2577 | ||
| TD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| TD：3.2 mm | 0.40 to 0.70 | % | ISO 2577 |
| MD：3.2 mm | 0.40 to 0.70 | % | ISO 2577 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 48 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | ASTM D256 | ||
| 23℃ | 44 | kJ/m² | ISO 180-1A |
| -30℃，3.2mm | 390 | J/m | ASTM D256 |
| -30℃，6.4mm | 200 | J/m | ASTM D256 |
| 23℃，3.2mm | 570 | J/m | ASTM D256 |
| 23℃，6.4mm | 420 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, annealed, 4.0 mm | 105 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 6.4 mm | 108 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 4.0 mm | 125 | ℃ | ISO 75-2/B |
| Vicat Softening Temperature | |||
| B50 | 123 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength | |||
| Broken BRK | 55.0 | MPa | ASTM D638 |
| Yield yld | 52.0 | MPa | ISO 527-2/50 |
| Yield yld | 57.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK | 80 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Strength | 78.0 | MPa | ASTM D790 |
| Flexural Strength | 82.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 113 | ASTM D785 | |
| R-level | 113 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | |||
| — | 90 to 100 | °C | |
| Hot air dryer | 90 to 100 | °C | |
| Drying Time | |||
| — | 2.0 to 4.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Maximum Moisture Content | 0.020 | % | |
| Rear Temperature Zone 1 | 210 to 230 | °C | |
| Middle Temperature Zone 2 | 230 to 250 | °C | |
| Front Temperature Zone 3 | 250 to 265 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Mold Temperature | 60 to 90 | °C | |
| Injection pressure | 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.11 in/min |
| 4. 0.079 in/min |
| 5. Thickness: 4mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |