| PC+ ABS混合20%玻璃增强，高耐热性，优秀的平衡强度和刚度，良好冲击性和外观 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Glass fiber reinforced |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, 50 mm/min | 94 | MPa | ASTM D638 |
| Fracture, 50 mm/min | 94 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 50 mm/min | 2.6 | % | ASTM D638 |
| Fracture, 50 mm/min | 2.6 | % | ASTM D638 |
| Tensile modulus | |||
| 5 mm/min | 2630 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 149 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3 mm/min，50mm跨距 | 5900 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 460 | J/m | ASTM D 4813 |
| -30℃ | 490 | J/m | ASTM D 4813 |
| Total energy of instrument impact, | |||
| 23℃ | 22 | J | ASTM D 3763 |
| -30℃ | 21 | J | ASTM D 3763 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 80 | J/m | ASTM D 256 |
| -30℃ | 60 | J/m | ASTM D 256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | |||
| 3.2mm | 129 | ℃ | ASTM D 648 |
| 6.4mm | 132 | ℃ | ASTM D 648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.29 | ASTM D792 | |
| Melt Flow Rate | |||
| 230℃，3.80kg | 16 | g/10min | ASTM D1238 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |