| About |
|---|
| Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 to 11 | g/10min | |
| 230℃，5.0kg | 15 to 30 | g/10min | |
| Shrinkage rate | |||
| MD | 2.0 to 3.0 | % | |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃，4mm | 60.0 to 120 | J/m | ASTM D6110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | ASTM D4065 |
| Melting temperature | 162 to 168 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 133 to 140 | ℃ | ASTM D3418 |
| Crystallization heat | 53.0 to 60.0 | J/g | ASTM D3418 |
| Fusion heat | 53.0 to 60.0 | J/g | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 kHz | 7.00 to 10.0 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.10 mm | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second, 2.00 mm | 73 to 80 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃，2 mm | 1400 to 2200 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃, 2 mm | 45.0 to 60.0 | MPa | |
| Fracture, 23 ℃, 2 mm | 30.0 to 50.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃, 2 mm | 5.0 to 10 | % | |
| Fracture, 23 ℃, 2 mm | 20 to 300 | % | |
| friction coefficient | |||
| With oneself – dynamic | 0.15 to 0.35 | ||
| With oneself – static | 0.20 to 0.40 | ||
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-10 wheels | 5.00 to 10.0 | mg | ASTM D4060 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 0.039 in/min |
| 3. Type IV, 2.0 in/min |
| 4. 2 m/s |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |