| About |
|---|
| Mineral filled grade with low warp, easy flow and smooth surface appearance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant. UL-Listing V-0 in natural and black at1.5mm thickness per UL 94 flame testing. Relative- Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance,Good liquidity,Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.74 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.0E-3 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 5.0E-3 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 105 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 10000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 125 | MPa | ISO 178 |
| compressive strength | |||
| 1% strain | 53.1 | MPa | ISO 604 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.2 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 35 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 195 | ℃ | ISO 306 |
| Melting temperature | 335 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 3.6E-5 | 1/℃ | ISO 11359-2 |
| MD | 1.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 46 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.031 | IEC 60250 | |
| Compared to the leakage tracing index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 170 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 315 to 325 | °C | |
| Barrel middle temperature | 320 to 330 | °C | |
| Barrel front temperature | 325 to 335 | °C | |
| Nozzle temperature | 335 to 345 | °C | |
| Processing (melt) temperature | 335 to 345 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 50.0 to 150 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |