| About |
|---|
| XENOYX2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad color space.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Ductility,Good liquidity,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume Rate | ISO 1133 | ||
| 265℃，2.16 kg | 12.0 | cm³/10min | |
| 300℃，1.2 kg | 26.0 | cm³/10min | |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.15 to 0.25 | % | |
| TD：3.2 mm | 0.30 to 0.40 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.020 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.040 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3800 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 50.0 | MPa | ASTM D638 |
| yield | 51.0 | MPa | ISO 527-2/5 |
| fracture | 35.0 | MPa | ASTM D638 |
| fracture | 37.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/5 |
| fracture | 7.0 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 3500 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.0 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 95 | kJ/m² | |
| 23℃ | 95 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 210 | J/m | ASTM D256 |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 14 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1600 | J/m | ASTM D4812 |
| -30℃ | 74 | kJ/m² | ISO 180/1U |
| 23℃ | 110 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 36.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 111 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 101 | ℃ | |
| Vicat Softening Temp | |||
| B120 | 118 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 75.0 | ℃ | UL 746 |
| Electrical performance | 75.0 | ℃ | UL 746 |
| Impact mechanical performance | 75.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95.0 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |