| About |
|---|
| MVR (300 °C/1.2 kg) 12 cm³/10 min; flame retardant; UL 94V-0/2.2 mm and 5VA/3.0 mm; medium viscosity; UV stabilized; easy release; injection molding – melt temperature 280 – 320 °C; available in transparent and translucent colors; electrical/electronic&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good stripping performance,Flame Characteristics,V-2,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 75.0 | MPa | ISO 527-2/50 |
| Yield, 23 ℃ | 75.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | 100 | % | ISO 527-2/50 |
| Yield, 23 ℃ | 5.0 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 7391 | ||
| -30 ℃, completely fractured | 8.0 | kJ/m² | ISO 7391 |
| 23 ℃, completely fractured | 8.0 | kJ/m² | ISO 7391 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 106 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 118 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 123 | ℃ | ISO 306 |
| B120 | 124 | ℃ | ISO 306/B120 |
| Relative temperature index | |||
| Electrical performance, 1.50 mm | 125 | ℃ | UL 746 |
| Strength mechanical performance, 1.50 mm | 85.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.50 mm | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 2.20 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 2.2 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 930 | ℃ | IEC 60695-2-13 |
| 2.2 mm | 930 | ℃ | IEC 60695-2-13 |
| 3 mm | 960 | ℃ | IEC 60695-2-13 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3000 µm | 88.0 | % | ISO 13468-2 |
| Haze | |||
| 3000 µm | 0.90 | % | ISO 14782 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MFLR,(,,)-18-9 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Based on ISO 180-A, 3 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |