| About |
|---|
| Infino TK-2046HM is a Polycyclohexylenedimethylene Terephthalate (PCT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Reflectors.&& |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | PCT |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| – | 1.61 | g/cm³ | ISO 1183 |
| 1.61 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 300℃，1.20kg | 20 | g/10min | ISO 1133 |
| 300℃，1.20kg | 20 | g/10min | ASTM D1238 |
| Ash Content | |||
| — | 41 | % | ISO 3451 |
| — | 41 | % | ASTM D5630 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 61.0 | MPa | ASTM D638 |
| yield | 620 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.5 | % | ASTM D638 |
| fracture | 1.5 | % | ISO 527-2/5 |
| Bending modulus | 7600 | MPa | ASTM D790 |
| Bending modulus | 77000 | MPa | ISO 178 |
| bending strength | 78.0 | MPa | ASTM D790 |
| bending strength | 800 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 13 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃，3.2mm | 29 | J/m | ASTM D256 |
| 23℃，6.4mm | 29 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 3.0 | kJ/m² | ISO 180-1A |
| 23℃，3.2mm | 160 | J/m | ASTM D256 |
| 23℃，6.4mm | 150 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| -5℃ | 16 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 250 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 250 | ℃ | ISO 75-2/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | ASTM D1925 | ||
| — | 4.0 | YI | ASTM D1925 |
| 3.20 mm | 4.0 | YI | ASTM D1925 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| — | 100 | °C | |
| Hot air dryer | 120 | °C | |
| Drying time | |||
| — | 4.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 285 to 290 | °C | |
| Barrel middle temperature | 295 | °C | |
| Barrel front temperature | 295 to 300 | °C | |
| Nozzle temperature | 300 | °C | |
| Mold temperature | 130 to 160 | °C | |
| Injection pressure | 118 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.11 in/min |
| 4. Thickness: 4mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |