| Reactive random terpolymer of ethylene, butyl acrylate and glycidyl methacrylate (epoxide function) produced by high-pressure polymerization process. Reactivity with -OH, -COOH, -NH2, -SH. Compatibility with PET, PBT, PPS, PE. Adhesion to metallic surface. Good thermal stability. APPLICATIONS Impact modification of thermoplastic polyesters (PBT/PET/PC) and their alloys (e.g. PC/PBT). Impact modification, flexibilization and tie layer of polyphenylene sulfides (PPS). Compatibilizer for thermoplastic polyesters / polyolefins blends (PET/PO, PBT/PO). Adhesion promoter onto metallic surface. Bitumen performance enhencer.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | AEM |
| Material Status | Commercial: Negative |
| Features | Good bond,Terpolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ISO 1183 , ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 to 11 | g/10min | ASTM D1238，ISO 1133 |
| Butyl acrylate composition | 23.0 to 28.0 | wt% | |
| Glycidyl Methacrylate Content | 6.0 to 9.0 | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -46.0 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | < 40.0 | ℃ | ISO 306/A , ASTM D1525 2 |
| Melting temperature | 71.0 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 , ISO 868 | ||
| Shaw A, molded | 81 | ASTM D2240 , ISO 868 | |
| Shaw’s D, molded | 25 | ASTM D2240 , ISO 868 | |
| Tensile modulus | |||
| Compression Molding | 9.00 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| Fracture, molded | 4.00 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 860 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 11.0 | MPa | ASTM D790 , ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |