INEOS LDPE 23H430

About
Applications 23H430 is suitable for a variety of general-purpose packaging films, liners, carrier bags and fine shrink film. It is also recommended for cross-linked foam as well as for blow-moulding applications. Benefits and Features 23H430 is an autoclave LDPE homopolymer. It offers the following properties: Good strength and dart drop resistance Good drawdown Low tendency to block If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&&

About

Applications 23H430 is suitable for a variety of general-purpose packaging films, liners, carrier bags and fine shrink film. It is also recommended for cross-linked foam as well as for blow-moulding applications. Benefits and Features 23H430 is an autoclave LDPE homopolymer. It offers the following properties: Good strength and dart drop resistance Good drawdown Low tendency to block If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&&

Product Description
Supplier	INEOS
Generic	LDPE
Material Status	Commercial: Active
Features	Good Rigidity,Good dissection,Crosslinked,Foaming performance,Low density,Homopolymer
Availabilitys	Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.923	g/cm³	ISO 1183/D
Melt Flow Rate
190℃，2.16kg	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient
Blown film	> 0.50		ASTM D1894

film	Nominal value	Unit	Test method
film thickness
test	50	µm
Tensile modulus
1% secant, 50 µ m, blow molded film	180	MPa	ISO 1184
tensile strength			ISO 1184
MD, yield, 50 µ m, blow molded film	11.0	MPa	ISO 1184
TD, yield, 50 µ m, blow molded film	12.0	MPa	ISO 1184
tensile strength			ISO 1184
MD, fracture, 50 µ m, blow molded film	22.0	MPa	ISO 1184
TD, fracture, 50 µ m, blow molded film	20.0	MPa	ISO 1184
Tensile strain			ISO 1184
MD, fracture, 50 µ m, blow molded film	250	%	ISO 1184
TD, fracture, 50 µ m, blow molded film	550	%	ISO 1184
Drop hammer impact
50 µ m, blow molded film	140	g	ASTM D1709-A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	95.0	℃	ISO 306/A

optical performance	Nominal value	Unit	Test method
gloss
45 °, 50.0 µ m, blow molded film	55		ASTM D2457
Haze
50 µ m, blow molded film	10	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	160 to 185	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.