| Rubber modified (PC+SAN) blend; 10% glass fibre reinforced; Vicat/B 120 temperature = 134°C; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 4800 MPa; good heat resistance&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+AS(SAN) |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good heat aging resistance,Good liquidity,High Heat Resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 4800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 95.0 | MPa | ISO 527-2/5 |
| Yield, 23 ℃ | 100 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.7 | % | ISO 527-2/5 |
| Yield, 23 ℃ | 3.2 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 6.0 | kJ/m² | ISO 180-A |
| 23℃ | 8.0 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -30℃ | 35 | kJ/m² | ISO 180 |
| 23℃ | 35 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 121 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 133 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 132 | ℃ | ISO 306 |
| B120 | 134 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 23℃，100 Hz | 3.20 | IEC 60250 | |
| 23℃，1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，100 Hz | 2.5E-3 | IEC 60250 | |
| 23℃，1 MHz | 9.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.90 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 2577 | ||
| TD：260℃，3.0 mm | 0.35 to 0.55 | % | ISO 2577 |
| MD：260℃，3.0 mm | 0.25 to 0.45 | % | ISO 2577 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 260℃ | 205 | Pa·s | ISO 11443-A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm,, MT 80°C |
| 3. 1000s-1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |