| About |
|---|
| AvaSpire® AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK)designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemical resistance expected of PEEK while maintaining excellent elevated temperature properties. The price and performance of this resin will expand the opportunities for PEEK resins especially in the area of metal replacement for corrosion control. Natural: AvaSpire® AV-750 GF40 NT&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Solvent resistance,V-1,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| — | 53 | J/m | ASTM D256 |
| — | 8.5 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| — | 590 | J/m | ASTM D4812 |
| — | 41 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 285 | ℃ | ASTM D648 |
| Glass transition temperature | 150 | ℃ | ASTM D3418 |
| Melting peak temperature | 345 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 1.5E-5 | 1/℃ | ASTM E831 |
| specific heat | DSC | ||
| 50℃ | 1260 | J/kg/℃ | DSC |
| 200℃ | 1620 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | 0.31 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume resistivity | 1.8E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | 19 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.68 | ASTM D150 | |
| 1 kHz | 3.69 | ASTM D150 | |
| 1 MHz | 3.66 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ASTM D150 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 3.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-1 | UL 94 | |
| 1.60 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 105 | ASTM D785 | |
| Tensile modulus | |||
| — | 15100 | MPa | ASTM D638 |
| — | 16700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Yield, 5 mm | 188 | MPa | ISO 527-2/1A/5 |
| — | 191 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.8 | % | ASTM D638 |
| fracture | 1.8 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| — | 14800 | MPa | ASTM D790 |
| — | 15400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 253 | MPa | ASTM D790 |
| 250℃ | 54.0 | MPa | ASTM D790 |
| — | 250 | MPa | ISO 178 |
| compressive strength | 182 | MPa | ASTM D695 |
| shear strength | 89.0 | MPa | ASTM D732 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 380℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：3.2 mm | 0.10 to 0.30 | % | ASTM D955 |
| TD：3.2 mm | 1.2 to 1.4 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 450 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 to 175 | °C | |
| Drying time | 2.5 to 4.0 | hr | |
| Processing (melt) temperature | 370 to 395 | °C | |
| Mold temperature | 175 to 210 | °C | |
| Back pressure | 0.138 to 0.345 | MPa | |
| Screw speed | 75 | rpm | |
| Screw compression ratio | 2.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Under normal molding conditions AvaSpire AV-750 GF40 has lower viscosity and higher flow than AV-650 GF30. |
| 3. 5″ x 0.5″ x 0.125″ bars |
| 4. 0.20 in/min |
| 5. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |