| 35% Glass Reinforced, Flame Retardant (halogen- phosphorous-free)&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.49 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.1 | % | |
| MD | 0.40 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.7 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12500 | MPa | |
| tensile strength | |||
| fracture | 200 | MPa | |
| Tensile strain | |||
| fracture | 2.5 | % | |
| Bending modulus | 12500 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 60 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 11 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 290 | ℃ | |
| 1.8 MPa, unannealed | 290 | ℃ | |
| Glass transition temperature | 75.0 | ℃ | |
| Melting temperature | 295 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 3.5E-5 | 1/℃ | |
| TD | 4.0E-5 | 1/℃ | |
| Relative temperature index | |||
| Electrical performance, 0.75 mm | 65.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | |
| Dielectric strength | 33 | kV/mm | |
| Relative permittivity | |||
| 100 Hz | 4.80 | ||
| 1 MHz | 4.40 | ||
| Dissipation factor | |||
| 100 Hz | 8.0E-3 | ||
| 1 MHz | 0.017 | ||
| Compared to the leakage tracing index | 425 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.75 mm | V-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 285 to 295 | °C | |
| Barrel middle temperature | 290 to 300 | °C | |
| Barrel front temperature | 295 to 300 | °C | |
| Nozzle temperature | 295 to 300 | °C | |
| Processing (melt) temperature | 295 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 0.500 to 3.00 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |