Kynar Flex® 2800-00

About
Kynar Flex® resins are fluorinated thermoplastic copolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties. Main applications: flexible tubing, corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable jacketing with and without cross-linking. Kynar Flex® 2800-00 resin is a standard grade of granules, compared to the homopolymer grades, which exhibits a lower modulus, a better resistance to stress cracking in alkaline and oxidizing media, and a lower melting point. For cable coating, extrusion of tube and plaque, compression molding of bulky parts. Additional characteristics: Easily processed using conventional equipment Excellent thermal stability Retains properties after aging Pigmentable UL RTI temperature rating 125°C Radiation crosslinking&&

About

Kynar Flex® resins are fluorinated thermoplastic copolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties. Main applications: flexible tubing, corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable jacketing with and without cross-linking. Kynar Flex® 2800-00 resin is a standard grade of granules, compared to the homopolymer grades, which exhibits a lower modulus, a better resistance to stress cracking in alkaline and oxidizing media, and a lower melting point. For cable coating, extrusion of tube and plaque, compression molding of bulky parts. Additional characteristics: Easily processed using conventional equipment Excellent thermal stability Retains properties after aging Pigmentable UL RTI temperature rating 125°C Radiation crosslinking&&

Product Description
Supplier	Arkema
Generic	PVDF
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,High impact resistance,Low temperature toughness,Solvent resistance,Heat Stabilized,High ESCR
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
THERMAL	Nominal value	Unit	Test method
Melting peak temperature	140 to 145	℃	ASTM D3418

Electrical performance	Nominal value	Unit	Test method
Volume resistivity
20 ℃	2.0E+14	ohms·cm	ASTM D257

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 23 ℃	60 to 70		ASTM D2240
tensile strength			ASTM D638
Yield, 23 ℃	20.0 to 34.5	MPa	ASTM D638
Fracture, 23 ℃	17.2 to 34.5	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	100 to 300	%	ASTM D638
Bending modulus
23℃	483 to 758	MPa	ASTM D790
bending strength
23℃	20.7 to 34.5	MPa	ASTM D790
compressive strength
23℃	31.0 to 41.4	MPa	ASTM D695

PHYSICAL	Nominal value	Unit	Test method
Density	1.77 to 1.80	g/cm³	ASTM D792
Apparent viscosity of melt
232℃，100 sec^-1	2200 to 2700	Pa·s	ASTM D3835

Notes
1. Typical properties: these are not to be construed as specifications.
2. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.