| About |
|---|
| AMPLIFY™ TY 3351 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 3351 Functional Polymer promotes adhesion of Polyethylene to polystyrene (HIPS) and barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates. Main Characteristics: Excellent adhesion to polyamide and EVOH For blown and cast film and sheet Complies with: U.S. FDA 21CFR175.105 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | 马来酸酐接枝共聚物 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| MAH grafting level | Low | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| yield | 12.0 | MPa | ASTM D638 |
| fracture | 9.42 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 480 | % | ASTM D638 |
| Bending modulus | |||
| 2% secant | 276 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 89.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 126 | ℃ | ASTM D4591 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |