| About |
|---|
| Description Transparency, Softeness, No Stress whitening Application the edge of furniture&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS transparent |
| Material Status | Commercial: Active |
| Features | Good Clarity,Soft,High ESCR |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 49 | J/m | |
| 23℃，6.4mm | 49 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 79.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 91.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 82 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 38.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 30 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 1620 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 58.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Processing (melt) temperature | 220 to 240 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | < 80 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |