PRIMACOR™ 3004

About
PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR). Excellent draw down and edge stability Excellent product resistance Excellent hot tack, heat seal, toughness High performance sealant or tie layer Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details.&&

About

PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR). Excellent draw down and edge stability Excellent product resistance Excellent hot tack, heat seal, toughness High performance sealant or tie layer Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	EAA
Material Status	Commercial: Negative
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.938	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate
190℃，2.16kg	8.5	g/10min	ASTM D1238，ISO 1133
Co monomer content	9.7	%

MECHANICAL	Nominal value	Unit	Test method
tensile strength			ASTM D638 , ISO 527-2
Yield, molding	7.93	MPa	ASTM D638 , ISO 527-2
Fracture, molded	17.6	MPa	ASTM D638 , ISO 527-2
Tensile strain
Fracture, molded	600	%	ASTM D638 , ISO 527-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	81.1	℃	ASTM D1525 , ISO 306
Melting temperature
DSC	98.0	℃	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	260 to 290	°C
Shrinkage (288°C, 25.4 μm)	50.8	mm
Minimum coating thickness	10	µm
Minimum coating weight	9.8	g/m²

Notes
1. Typical properties: these are not to be construed as specifications.
2. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.