| 高流动,耐候・易脱模型・ 冰色 |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile (yield) strength | 65 | MPa | ISO 527-1 |
| Tensile strain | |||
| fracture | 95 | % | ISO 527-1 |
| bending strength | 90 | MPa | ISO 178 |
| Bending elasticity | 2.3 | GPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 50 | ISO 2039-2 | |
| R-level | 120 | ISO 2039-2 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | ISO 75-1/2 | ||
| 1.8 MPa | 125 | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | 6.5 | ×10-5/℃ | ISO 11359-2 |
| 成型收缩率 | |||
| MD：2 mm | 0.5～0.7 | % | 出光法 |
| TD：2 mm | 0.5～0.7 | % | 出光法 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2/0.4-1.8 | mm | UL 94 |
| Resistance to conductive tracks | 2 | PLC | UL746A |
| Temperature index | |||
| Electrical performance | 130 | ℃ | UL746B |
| IMPACT | 125 | ℃ | UL746B |
| static state | 130 | ℃ | UL746B |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 85～89 | % | ISO 13468-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Voltage resistance | |||
| breakdown voltage | 30 | kV/mm | IEC 60243-1 |
| Arc resistance | 6 | PLC Code | ASTM D495 |
| Volume resistivity | １E+16< | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 1 MHz | 2.85 | IEC 60250 | |
| Dielectric loss | |||
| 1MHz | 0.0092 | IEC 60250 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 70 | kJ/m² | ISO 179-1 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 24h，50% RH | 0.23 | % | ISO 62 |
| 体积流动速率(MVR) 300℃ 1.20kg | 19 | cm³ /10min | ISO 1133 |
| Spiral flow length | |||
| SFL | 20 | cm | 出光法 |
| Process Conditions | |||
|---|---|---|---|
| Standard forming conditions | Nominal value | Unit | Test method |
| Barrel temperature | 260～300 | ℃ | |
| Mold temperature | 80～120 | ℃ | |
| Dry conditions | 120℃、5～8小时 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |