| About |
|---|
| Thermal conductive material, Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Thermal conductivity,V-0 |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 | % | ISO 294-4 |
| MD | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.60 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | ASTM E1461 | ||
| — | 2.1 | W/m/K | ASTM E1461 |
| — | 14 | W/m/K | ASTM E1461 |
| Relative temperature index | |||
| Electrical performance, 0.75 mm | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+6 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 280 to 320 | °C | |
| Barrel middle temperature | 300 to 320 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 305 to 335 | °C | |
| Processing (melt) temperature | 305 to 325 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 2.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Through Plane |
| 3. In Plane |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |